Armanios / Ltd Fracture of Composites
Erscheinungsjahr 1996
ISBN: 978-3-0357-0360-3
Verlag: Trans Tech Publications
Format: PDF
Kopierschutz: 0 - No protection
E-Book, Englisch, 612 Seiten
ISBN: 978-3-0357-0360-3
Verlag: Trans Tech Publications
Format: PDF
Kopierschutz: 0 - No protection
The potential of composites cannot be fully realized unless their fracture modes and failure mechanisms are fully understood, and appropriate design tools for failure prediction are developed and verified.
Autoren/Hrsg.
Weitere Infos & Material
Preface
Mechanics of Anisotropic Materials with Multiple Cracks
Energy Release Rate for Cracks on a Non-Planar Interface
Strength and Fracture of a Composite with Well Aligned Fibers
Analysis of Free Edge Delamination in Unsymmetrical Composite Laminates
On the Numerical Modelling of Edge Delamination in Composites
Analytical Determination of Mixed-Mode Energy Release Rates for Delamination Using a Crack Tip Element
Computational Structural Analysis and Testing: An Approach to Understand Delamination Growth
Using Stress Smoothing for Interlaminar Stress Distribution in Finite Element Analysis of Composite Laminates
Damage Mechanisms and Fracture Modes in Nicalon / CAS-II Laminates
Recent Research on Damage Development in SiC/Ti Continuous Fiber Metal Matrix Composites
Failure Prediction of Composite Laminates under Torsion
Stress Determination and Core Failure Analysis in Sandwich Rampdown Structures under Bending Loads
Interlaminar Fracture Characterization
Fracture of Double Beam Specimens Containing 90-Degree Plies
Application of the MMB Specimen in the Measurement of Mixed Mode Interlaminar Fracture Toughness
Notch Effect on Fatigue of High Performance Composite Materials Mechanisms and Prediction
Buckling of Pressure-Loaded, Delaminated, Cylindrical Shells and Panels
Snap Buckling of Thin Delaminated Layers in a Contracting Cylinder
Predicting the Growth of Internal Delaminations under Monotonic or Cyclic Compression
Failure Mechanisms of Composite Plates with a Circular Hole under Remote Static Biaxial Planar Compressive Loading
Fracture of Laminated Composites with Interleaves
Transverse Cracking of Composite Laminates with Interleaves: A Variational Approach
Low-Velocity Impact Response and Damage in Composite Materials
Fracture of Marine Composites